STUDI PENGARUH VARIASI SUHU KALSINASI TERHADAP KEKERASAN BENTUK MORFOLOGI, DAN ANALISIS POROSITAS NANOKOMPOSIT CAO/SiO2 UNTUK APLIKASI BAHAN BIOMATERIAL

Authors

  • Akhmad Kurniawan Jurusan Fisika FMIPA Universitas Negeri Surabaya
  • Muchammad Nizar Jurusan Fisika FMIPA Universitas Negeri Surabaya
  • Muhammad Rijal Jurusan Fisika FMIPA Universitas Negeri Surabaya
  • Redy Bagas Jurusan Fisika FMIPA Universitas Negeri Surabaya
  • Woro Setyarsih Jurusan Fisika FMIPA Universitas Negeri Surabaya

DOI:

https://doi.org/10.26740/jpfa.v4n2.p22-26

Keywords:

Biomaterial, nanocompositeCaO/SiO2, Hardness Vickers, SEM, BET

Abstract

Biomaterial substance is needed by citizen, but the suplayed is limited and expansive. It become inspirations give new efisience inovations biomaterial subtance from nature. For that research is done which has purpose to make biomaterial subtance from eggsheld waste and mud. Method which is used are nanocomposite CaO/SiO2 syntesis and mix by ratio 2:1., than calcinations by temperature 700oC, 800oC, 900oC, than caracterize use hardness vickers, SEM, BET test. The result of caracteritation of show that at 900oC the quality highest hardness receand is 109,1 ± 5,22 VHN. Than microstructure where in this temperature granula which clod and became bigger the pore little. Where as for its porositation analyzed at this temperature of surface value is 23.843 m2/g and pore volume is 0.007 cc/g. From the analysis can get conclutions that the increasing by temperature of calcinations coused hardness quality increase and influence microstructure also surface area at the sample surface.

References

Kurniawan, A., M., Nizar, M., Rijal, Redy Bagas. 2014. Study Pengaruh Suhu Kalsinasi Terhadap Sifat Kekerasan dan Mikrostruktur CaO/SiO2 Untuk Aplikasi Bahan Biomaterial. Prosiding Seminar dan Lokakarya Nasional Fisika 2014. Unesa.

Arifin, Fatahul dan Eka Satria Martomi. 2009. Keramik (Advance Ceramics) Sebagai Material Alternatif di Bidang Kesehatan. Jurnal Austenit. 1(1): April 2009.

Cahyanto, Arief. 2009. Makalah Biomaterial. Bogor : Institut Pertanian Bogor

Federman, R., S., H., S., Mansur, E., F., B., Stancioli. 2009. Biocompatibility evaluation of SiO2-CaO/stainless steel composite bioactive film for biomedical application. Instituto Nacional da Propriedade Industrial Portugal.

Jin-Bo, LI, LI Xuan Yong, LI Wei Feng, ZHOU Jiang Hao . 2011. Preparation and Characterization of Bioactive Poly (Lactic Acid)/SiO2-CaO Composite Membranes. Journal of inorganic materials.26(9).

Lukman. M., W., Yudyanto, Hartatiek (2012). Artikel Sintesis biomaterial Komposit CaO-SiO2 Berbasis Material Alam (Batuan Kapur dan Pasir Kuarsa) dengan Variasi Suhu Pemanasan dan Pengaruhnya Terhadap Porositas, Kekerasan dan Mikrostruktur. Universitas Negeri Malang. 2012.

Januar, Akhmad., P. 2013. Pengaruh pH Akhir Larutan Pada Sintesis Nanosilika Dari Bahan Lusi dengan Metode Kopresipitasi. Universitas Negeri Surabaya. 2013

Rahmawati, I., Nurjanah. 2013. Pengaruh Variasi Kecepatan Aliran Gas CO2 Terhadap Kemurnian dan Ukuran Kristal Nanokalsit dari Cangkang Kerang Bulu dengan Metode Karbonasi. Universitas Negeri Surabaya. 2013

Rahmawati, Sari., dkk. 2012. Sintesis Partikel Nano CaO Dengan Metode Kopresipitasi Dan Karakterisasinya. FMIPA. ITS. 2012

Munasir, Triwikantoro. 2010. Sintesis Gel Orde Nano dari Lumpur Sidoarjo (Lusi) dan Prospek Aplikasinya. Universitas Negeri Surabaya. 2010.

Downloads

Published

2014-12-14

How to Cite

Kurniawan, A., Nizar, M., Rijal, M., Bagas, R. and Setyarsih, W. (2014) “STUDI PENGARUH VARIASI SUHU KALSINASI TERHADAP KEKERASAN BENTUK MORFOLOGI, DAN ANALISIS POROSITAS NANOKOMPOSIT CAO/SiO2 UNTUK APLIKASI BAHAN BIOMATERIAL”, Jurnal Penelitian Fisika dan Aplikasinya (JPFA), 4(2), pp. 22–26. doi: 10.26740/jpfa.v4n2.p22-26.

Issue

Section

Articles
Abstract views: 1749 , PDF Downloads: 2321