ANALISA VARIASI ARUS PENGELASAN SS 304 MENGGUNAKAN SHIELDED METAL ARC WELDING (SMAW) TERHADAP KEKUATAN MEKANISNYA

Authors

  • Nidia Lestari Institute Sains & Technology AKPRIND, Yogyakarta

DOI:

https://doi.org/10.26740/otopro.v16n1.p18-22

Keywords:

SMAW, Stainless Steel 304, current variation, mechanical properties

Abstract

Austenitic stainless steel or commonly known as AISI 304 stainless steel has advantages, including good ductility at relatively low temperatures and high resistance to corrosion. These properties make Austenitic Stainless Steel a candidate material for use in pipe fabrication systems, automotive exhaust gas systems and some equipment related to the chemical and nuclear industry. Therefore, it is necessary to analyze the variation of welding currents on the strength of the welds in the application of Shielded Metal Arc Welding (SMAW) on stainless steel. The electrodes used are E308-16 types with current variations of 90 amperes, 100 amperes and 110 amperes. The results showed that the electric current factor in the SMAW welding process greatly influenced the welding results in terms of its strength. The highest mechanical strength was obtained at welding current of 110 Ampere, with a heat input of 976.067 J / mm, an average mechanical strength of 68.438 kg / mm2 for tensile stress and strain of 47.451% in the tensile test, and an average value of hardness of 225.008 HV for hardness test in weld.

References

AWS A5.4. 1992. Specification for Stainless Steel Electrodes for Shielded Metal Arc Welding. Miami: American Welding Society Inc.

ASM Handbook Vol 9. 2004. Metallography And Microstructure. ASM

Wiryosumarto, H dan Toshie Okumura. 2004. Teknologi Pengelasan Logam. Cetakan Kesembilan. Jakarta: Pradnya Paramita.

Sofyan, Bondan T. 2011. Pengantar Material Teknik. Cetakan Keempat. Jakarta: Salemba Teknika.

Nasrul, M. Yogi, Suryanto, H., & Qolik, A. (2017). Pengaruh Variasi Arus Las SMAW Terhadap Kekerasan dan Kekuatan Tarik Sambungan Dissimilar Stainless Steel 304 dan ST 37. JURNAL TEKNIK MESIN, 24(1).

ASTM E8/E8M 13. 2013. Standard Test Methods for Tension Testing of Mettalic Materials. United States: ASTM International.

ASTM E92-82.1997 Standard Test Methods for Vickers Hardness of Mettalic Materials. United States: ASTM International.

Azwinur, A., Jalil, S. A., & Husna, A. (2017). Pengaruh variasi arus pengelasan terhadap sifat mekanik pada proses pengelasan SMAW. Jurnal POLIMESIN, 15(2), 36-41.

Daryanto. 2013. Teknik Las. Cetakan Kedua. Bandung: Alfabeta.

Parekke, S. (2017). Pengaruh Variasi Arus Pada Pengelasan SMAW Dan GTAW Terhadap Sifat Mekanis Dan Fisis Pada Logam Berbeda Baja Karbon Sedang Dengan Baja Tahan Karat Austenit. Dinamika: Jurnal Ilmiah Teknik Mesin, 9(1), 12-19.

Setiawan, A. (2016). œPenelitian Stainless Steel 304 Terhadap Pengaruh Pengelasan Gas Tungsten Arc Welding (GTAW) Untuk Variasi Arus 50 A, 100 A dan 160 A Dengan Uji Komposisi Kimia, Uji Struktur Mikro, Uji Kekerasan Dan Uji Impact (Doctoral dissertation, Universitas Muhammadiyah Surakarta).

Downloads

Published

2020-11-25

Issue

Vol 16 No 1 Nov 2020

Section

Article

License

Authors who publish with this journal agree to the following terms:

    1. Authors retain copyright and grant the journal right of first publication with the work simultaneously licensed under a  Creative Commons: Attribution-NonCommercial 4.0 International (CC BY-NC) that allows others to share the work with an acknowledgement of the work's authorship and initial publication in this journal.
    2. Authors are able to enter into separate, additional contractual arrangements for the non-exclusive distribution of the journal's published version of the work (e.g., post it to an institutional repository or publish it in a book), with an acknowledgement of its initial publication in this journal.
Abstract views: 490 , PDF Downloads: 1420